Análisis de materiales bioactivos en consistencia putty para el sellado de perforaciones del piso pulpar mediante un modelo ex vivo
| dc.contributor.advisor | Retana Lobo, Cristina | |
| dc.contributor.author | Núñez Vásquez, María Fernanda | |
| dc.contributor.author | Salazar Quesada, Andrea | |
| dc.date.accessioned | 2025-03-03T21:36:38Z | |
| dc.date.available | 2025-03-03T21:36:38Z | |
| dc.date.issued | 2023 | |
| dc.description | Tesis (licenciatura en odontología)--Universidad de Costa Rica. Facultad de Odontología, 2023 | |
| dc.description.abstract | Objetivo. Analizar las propiedades adhesivas y de biomineralización de diferentes materiales bioactivos en consistencia putty mediante un modelo ex vivo que simule las condiciones de perforación del piso pulpar. Metodología. Se simuló un microambiente ex vivo de la región periapical. Para esta etapa fueron utilizados 12 molares para cada grupo que dio un total de 48 muestras, a los cuales se les cortó, con ayuda de un disco de diamante, las coronas en la unión amelo-cemento. Se realizaron perforaciones de furca en el piso pulpar de las piezas con una fresa de carburo #6 previamente calibrada, para obtener perforaciones de 1.8 mm aproximadamente, las cuales fueron selladas con los materiales bioactivos experimentales los cuales fueron MTA, Bio-C® Repair, NeoPutty™ y MTA Flow™, seguidamente fueron colocadas en PBS para simular los tejidos periapicales durante el tiempo experimental. Las muestras fueron divididas aleatoriamente. Dos de estas se colocaron en recipientes de plástico, previamente identificados, con 20 mL de PBS (pH = 7,2) y las restantes 10, se colocaron en espuma floral humedecida con PBS (pH = 7,2) para simular los tejidos periapicales. Todas se mantuvieron a 37°C durante 30 días. Resultados. Con respecto a la prueba de resistencia “push out” se determinó que de acuerdo con los datos obtenidos y evaluados estadísticamente con el programa GraphPad Prism 10.1, se pudo observar que las muestras no presentaron diferencias estadísticamente significativas entre los distintos grupos de materiales utilizados en el momento de realizar la prueba. De igual forma se tomaron las muestras y se observaron todos los grupos de trabajo en el microscopio, donde se detalló que, en el momento de realizar el test, los modos de fallo fueron en su mayoría de tipo cohesivos. También todos los materiales utilizados mostraron la capacidad de realizar la liberación de iones calcio, sin embargo, el grupo 4 NeoPutty™ fue el material que obtuvo... | es_CR |
| dc.description.abstract | Inglés: Objective. Analyze the adhesive and biomineralization properties of different bioactive materials in putty consistency using an ex vivo model that simulates the drilling conditions of the pulp floor. Methodology An ex vivo microenvironment of the periapical region was simulated. For this stage, 12 molars were used for each group, giving a total of 48 samples, from which the crowns at the amelo-cementum junction were cut with the help of a diamond disc. Furcation perforations were made in the pulpal floor of the pieces with a previously calibrated #6 carbide drill, to obtain approximately 1.8 mm perforations, which were sealed with the experimental bioactive materials which were MTA, Bio-C® Repair, NeoPutty™ and MTA Flow™; then placed in PBS to simulate periapical tissues during the experimental time. The samples were divided randomly. Two of these were placed in plastic containers, previously identified, with 20 mL of PBS (pH = 7.2) and the remaining 10 were placed in floral foam moistened with PBS (pH = 7.2) to simulate periapical tissues. All were kept at 37°C for 30 days. Results The "push out" resistance test, it was determined that according to the data obtained and statistically evaluated with the GraphPad Prism 10.1 program, it was 14 observed that the samples did not present statistically significant differences between the different groups of materials used in the time to perform the test. In the same way, the samples were taken, and all the work groups were observed under the microscope, where it was detailed that, at the time of carrying out the test, the failure modes were mostly of the cohesive type. All the materials used also showed the ability to release calcium ions, however, group 4 NeoPutty™ was the material that obtained the greatest amount of calcium ions from day 3 (4.2 Mg/L) and was maintained high levels compared to the other groups until day 30 (3.6 Mg/L). Furthermore, the formation of the biomineralization interface... | |
| dc.description.procedence | UCR::Docencia::Salud::Facultad de Odontología | |
| dc.identifier.uri | https://repositorio.sibdi.ucr.ac.cr/handle/123456789/24132 | |
| dc.language.iso | spa | |
| dc.subject | BIOMINERALIZACION | |
| dc.subject | CEMENTO DENTAL | |
| dc.subject | COMPUESTOS BIOACTIVOS | |
| dc.subject | MATERIALES DENTALES - PRUEBAS | |
| dc.subject | SELLADORES DE FOSAS Y FISURAS (ODONTOLOGIA) | |
| dc.title | Análisis de materiales bioactivos en consistencia putty para el sellado de perforaciones del piso pulpar mediante un modelo ex vivo | |
| dc.type | proyecto fin de carrera |