Evaluación de la liberación de iones Ca2+, pH y resistencia a la flexión de cuatro cementos selladores endodónticos bioactivos
| dc.contributor.advisor | Benavides García, Marianella | |
| dc.contributor.author | Infante Amore, Fiorella | |
| dc.contributor.author | Ramírez Hidalgo, Eladio | |
| dc.contributor.author | Suárez Quesada, Luis Carlos | |
| dc.date.accessioned | 2024-11-29T21:26:32Z | |
| dc.date.available | 2024-11-29T21:26:32Z | |
| dc.date.issued | 2023 | |
| dc.description | Seminario de graduación (licenciatura en odontología)--Universidad de Costa Rica. Facultad de Odontología, 2023 | |
| dc.description.abstract | El objetivo de este estudio fue evaluar la liberación de iones de calcio, la resistencia a la flexión y el pH de los cementos endodónticos bioactivos ProRoot MTA ®, BIODENTINE ® y Bio C Repair ® y NeoPutty ®. Para evaluar la liberación de calcio se utilizaron 34 discos de 2 mm de dentina radicular estandarizados en el conducto con Gates Glidden número 6, obturados y sumergidos en una solución de 10 ml de PBS, se realizaron mediciones con pHímetro y espectrometría atómica al día 1, 3 5, 10 y 15. En cuanto a la prueba de resistencia a la flexión, se confeccionaron moldes de 10 barras de 7 mm x 2 mm x 2 mm de cada material, almacenados en recipientes herméticos con humedad durante 48 horas, estos especímenes se sometieron a la prueba mini-flex. Resultados: Los discos de dentina obturados con el Biodentine obtuvieron una menor liberación de calcio y presentaron una diferencia estadísticamente significativa (p=< 0.01) con respecto a los otros cementos; en la prueba de resistencia a la flexión el ProRoot MTA, se presentó mayor fuerza flexural; sin embargo, no hubo diferencia estadísticamente significativa (p=>0.05) entre los cementos. Se concluye que el NeoPutty es el material con mayor liberación de iones de calcio a lo largo de los 15 días y ProRoot MTA obtuvo mayor resistencia a la flexión. | es_CR |
| dc.description.abstract | Inglés: The objective of this study was to evaluate the calcium ion release, flexural strength and pH of the bioactive endodontic cements ProRoot MTA ®, BIODENTINE ® and Bio C Repair ® and NeoPutty ®. To evaluate calcium release, 34 2 mm discs of standardized root dentin were used in the canal with Gates Glidden number 6, filled and immersed in a 10 ml PBS solution. Measurements were carried out with a pH meter and atomic spectrometry on day 1. 3 5, 10 and 15. Regarding the flexural strength test, molds were made of 10 bars of 7 mm x 2 mm x 2 mm of each material, stored in airtight containers with humidity for 48 hours, these specimens were subjected to the mini-flex test. Results: The dentin discs filled with Biodentine obtained a lower calcium release, presenting a statistically significant difference (p=< 0.01) with respect to the other cements; In the flexural strength test, the ProRoot MTA presented greater flexural strength; however, there was no statistically significant difference (p=>0.05) between the cements. It is concluded that NeoPutty is the material with the highest release of calcium ions over the 15 days and ProRoot MTA obtained the highest flexural resistance. | |
| dc.description.procedence | UCR::Docencia::Salud::Facultad de Odontología | |
| dc.identifier.uri | https://repositorio.sibdi.ucr.ac.cr/handle/123456789/23631 | |
| dc.language.iso | spa | |
| dc.subject | CEMENTO DENTAL | |
| dc.subject | CONCENTRACION DE HIDROGENIONES | |
| dc.subject | DENTINA | |
| dc.subject | ESPECTROMETRIA | |
| dc.subject | FLEXIBILIDAD | |
| dc.subject | IONES DE CALCIO | |
| dc.subject | MATERIALES DENTALES - EVALUACION | |
| dc.title | Evaluación de la liberación de iones Ca2+, pH y resistencia a la flexión de cuatro cementos selladores endodónticos bioactivos | |
| dc.type | proyecto fin de carrera |